Among the many aluminum rod models starting with 6, they are mainly suitable for extrusion materials. For example, 6061 aluminum rods are suitable for manufacturing trucks, mechanical parts, precision machining, etc.; 6066 aluminum rods are suitable for extrusion of forgings and welded structures. Material. The aluminum rod named 6063 belongs to architectural profiles and is a representative alloy for extrusion. Compared with other types of aluminum rods, it is more suitable for special aluminum profiles for greenhouses. It is mainly reflected in the following four points. Please take a look with the editor. Bar!
1.6063 aluminum rod is a representative alloy for extrusion. It is strengthened by heat treatment and has high impact toughness;
2.6063 aluminum rods have excellent thermoplasticity and can be extruded at high speed into various profiles with complex structures, thin walls, and hollows or forged into forgings with complex structures;
3.6063 aluminum rod has excellent welding performance and corrosion resistance, and has no tendency to stress corrosion cracking. Among aluminum alloys that can be strengthened by heat treatment, Al-Mg-Si alloy is the only alloy in which no stress corrosion cracking phenomenon has been found.
The surface of 4.6063 aluminum rods is very smooth and clean after processing, and it is easy to anodize and color, making it more beautiful in use.
After long-term scientific verification, the aluminum extruded from 6063 aluminum rods when used in greenhouses has a smooth and tidy appearance, better corrosion resistance, high compressive strength, and longer service life.
Introduction to 6063 aluminum rod
Product name: 6063 aluminum rod, 6063 aluminum alloy rod
Material name: 6063 aluminum rod
Standard: GB/T 3191-1998
Main features and application scope of 6063 aluminum rod:
It is a low alloyed Al-Mg-Si high plasticity alloy.
Has many valuable features:
1. Strengthened by heat treatment, with high impact toughness and insensitivity to dispensing.
2. It has excellent thermoplasticity and can be extruded at high speed into various profiles with complex, thin-walled, and hollow structures or forged into forgings with complex structures. It has a wide quenching temperature range and low quenching sensitivity. After extrusion and forging demoulding, As long as the temperature is higher than the quenching temperature. It can be quenched by spraying water or water penetration. Thin-walled parts (6<3mm) can also be air-quenched.
3. Excellent welding performance and corrosion resistance, no tendency of stress corrosion cracking. Among aluminum alloys that can be strengthened by heat treatment, Al-Mg-Si alloy is the only alloy in which no stress corrosion cracking phenomenon has been found.
4. The surface after processing is very smooth and easy to anodize and color. The disadvantage is that if it is parked at room temperature for a period of time after quenching, it will have an adverse effect on the strength (parking effect).
Chemical composition of 6063 aluminum rod:
Silicon Si: 0.20～0.60
Copper Cu: 0.10
Magnesium Mg: 0.45～0.9
Zinc Zn: 0.10
Manganese Mn: 0.10
Titanium Ti: 0.10
Chromium Cr: 0.10
Iron Fe: 0.35
Aluminum Al: balance
Single: 0.05 Total: 0.15